Wear and corrosion interaction of aisi d2 in an acidic environment
Por:
Garcia T., Zeinert A., Muhl S., Lejeune M.
Publicada:
1 ene 2021
Resumen:
The tribological, electrochemical and tribo-electrochemical behavior of bare AISI D2 was studied. The tribological aspects were tested by pin on disc with an aluminum oxide ball as counter body, the electrochemical tests were performed in an aqueous solution of citric acid and the tribo-electrochemical evaluation was through a combination of both tests. AISI D2 steel presented abrasive wear in dry and wet conditions, such type of wear occurred due to stick-slip motion, moreover, in wet conditions the alloy corroded at corrosion current values around 10-6 A/cm2. The damage produced over the wear track was larger under wet conditions than for the dry conditions. © 2021 Helsinki University of Technology. All rights reserved.
Filiaciones:
Garcia T.:
Université de Picardie Jules Verne, 33 rue Saint Leu, Amiens, 80000, France
Zeinert A.:
Université de Picardie Jules Verne, 33 rue Saint Leu, Amiens, 80000, France
Muhl S.:
Instituto de Investigaciones en Materiales, Universidad Nacional Autónoma de México, Circuito Exterior S/N, Circuito de la Investigación Científica, Ciudad Universitaria, Ciudad de México, 04510, Mexico
Lejeune M.:
Université de Picardie Jules Verne, 33 rue Saint Leu, Amiens, 80000, France
Bronze
|