Mineral trioxide aggregate enriched with iron disulfide nanostructures: an evaluation of their physical and biological properties
Por:
Argueta-Figueroa, Liliana, Delgado-Garcia, Jose J., Garcia-Contreras, Rene, Martinez-Alvarez, Omar, Santos-Cruz, Jose, Oliva-Martinez, Carlos, Acosta-Torres, Laura S., de la Fuente-Hernandez, Javier, Arenas-Arrocena, Ma C.
Publicada:
1 jun 2018
Categoría:
Dentistry (miscellaneous)
Resumen:
The purpose of this study was to characterize mineral trioxide aggregates (MTA) enriched with iron disulfide (FeS2) nanostructures at different concentrations, and to investigate their storage modulus, radiopacity, setting time, pH, cytotoxicity, and antimicrobial activity. Iron disulfide nanostructures [with particle size of 0.357 ± 0.156 µm (mean ± SD)] at weight ratios of 0.2, 0.4, 0.6, 0.8, and 1.0 wt% were added to white MTA (wMTA). The radiopacity, rheological properties, setting time, and pH, as well as the cytotoxicity (assessed using the MTT assay) and antibacterial activity (assessed using the broth microdilution test) were determined for MTA/FeS2 nanostructures. The nanostructures did not modify the radiopacity values of wMTA (~6 mm of aluminium); however, they reduced the setting time from 18.2 ± 3.20 min to 13.7 ± 1.8 min, and the storage modulus was indicative of a good stiffness. Whereas the wMTA/FeS2 nanostructures did not induce cytotoxicity when in contact with human pulp cells (HPCs) and human gingival fibroblasts (HGFs), they showed bacteriostatic activity against Staphylococcus aureus, Escherichia coli, and Enterococcus faecalis. Adding FeS2 nanostructures to MTA might be an option for improving the root canal sealing and antibacterial effects of wMTA in endodontic treatments. © 2018 Eur J Oral Sci
Filiaciones:
Argueta-Figueroa, Liliana:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
Delgado-Garcia, Jose J.:
División de Ciencias e Ingenierías Universidad de Guanajuato León, Guanajuato México
Univ Guanajuato, Div Ciencias & Ingn, Guanajuato, Mexico
Garcia-Contreras, Rene:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
Martinez-Alvarez, Omar:
Departamento de Ingeniería en Energía Universidad Politécnica de Guanajuato Guanajuato México
Univ Guanajuato, Dept Ingn Energia, Guanajuato, Mexico
Santos-Cruz, Jose:
Facultad de Química Energía-Materiales Universidad Autónoma de Querétaro Querétaro México
Univ Autonoma Queretaro, Fac Quim, Energia Mat, Queretaro, Mexico
Oliva-Martinez, Carlos:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
Acosta-Torres, Laura S.:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
de la Fuente-Hernandez, Javier:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
Arenas-Arrocena, Ma C.:
Laboratorio de Investigación Interdisciplinaria Área de Nanoestructuras y Biomateriales Escuela Nacional de Estudios Superiores Unidad León Universidad Nacional Autónoma de México León, Guanajuato México
Univ Nacl Autonoma Mexico, Escuela Nacl Estudios Super Unidad Leon, Area Nanoestruct & Biomat, Lab Invest Interdisciplinaria, Blvd UNAM 2011, Guanajuato 37684, Mexico
|